| Item | Condition | Method | Unit | Index | |
| Property | Melt Flow Rate | 220℃/10KG/S | ASTM D-1238 | g/10min | 14.60 |
| Water Absorption | / | ASTM D-570 | % | 0.30 | |
| Refractive index | / | ASTM D-542 | / | / | |
| Light transmittance | / | ASTM D-1003 | % | / | |
| Physical | Density | / | ASTM D-792 | / | 1.08 |
| Shrinkage factor | / | ASTM D-955 | % | 0.002-0.004 | |
| Mechanical | Flexural Strength | / | ASTM D-790 | Kg/cm2 | 1120 |
| Rockwell hardness | / | ASTM D-785 | M scale | 98 | |
| Tensile Strength | / | ASTM D-638 | Kg/cm2 | 660 | |
| Flexural drawing recovery | / | ASTM D-790 | % | 7 | |
| Tensile Strength | / | ASTM D-638 | Kg/cm2 | 46 | |
| IZODnotch impact strength | / | ASTM D-256 | Kj/m2 | 19 | |
| Thermal | Vicat softening point | / | ASTM D-1525 | ℃ | 97 |
| Deflection Temperature | no anneal | ASTM D-648 | ℃ | 83 | |
| Deflection Temperature | anneal | ASTM D-648 | ℃ | 87 | |
| Combustion Performance | / | UL94 | CLASS | HB | |
| Instruction | 1. Drying treatment needed before used.
2. Could be blended with ASA from other trade mark to extrution or injection. 3. Could be blended with AS from other trade mark to extrution or injection. 4. Could be blended with PC from other trade mark to extrution or injection. 5. Could be blended with ABS from other trade mark to extrution or injection. 6. Could be blended with PVC from other tradi mark to extrution or injection. |
||||